The Structural and Microwave Dielectric Properties of the BMT Ceramics with Sintering Temperature and BCN Composition Ratio |
| Authors |
최의선(Choe, Ui-Seon) ; 이문기(Lee, Mun-Gi) ; 류기원(Ryu, Gi-Won) ; 이성갑(Lee, Seong-Gap) ; 이영희(Lee, Yeong-Hui) |
| Keywords |
Quality factor(Q×f_ 0/) ; Dielectric constant(ε_ r/) ; Complex perovskite structure ; Temperature coefficient of resonant frequency(τ_ f/) |
| Abstract |
The microwave dielectric properties of Ba(Mg_{1}3/Ta_{2}3/O_3-Ba(Co_{1}3/Nb_{2}3/O_3[BMT-BCN] ceramics were investigated. The specimens were prepared by the conventional mixed oxide method with the sintering temperature of 1525°C~1575°C. It was found that Ba(Mg_{1}3/Ta_{2}3/O_3[BMT] and BCN formed a solid solution with complex perovskite structure. As increasing the mole fraction of BCN, dielectric constant increased while the temperature coefficient of resonant frequency was changed from positive to negative value. The highest value of quality factor, Q×f_{0}=138,205GHz, obtained in the 0.9BMT-0.1BCN ceramics sintered at 1575°C. In the range of x geq0.4, the dielectric constant was about 30. The 0.55BMT-0.45BCN ceramics sintered at 1525°C for 5 hours showed the microwave dielectric properties of ε_{r}=30.21, Q×f_{0}=85,789GHz and τ_{f}=2.9015ppm/°C.EX>. |