Mechanical Properties and Smoothness of Semiconductive Materials(Shield) in Power Cable |
| Authors |
양종석(Yang Jong-Seok) ; 이용성(Lee Yong-Sung) ; 박대희(Park Dae-Hee) ; 이경용(Lee Kyoung-Yong) |
| Abstract |
We have investigated thermal properties showed by changing the content of carbon black which is the component parts of semiconductive shield in underground power transmission cable. Specimens were made of sheet with the nine of those for measurement. Density of specimens was measured by density meter, and then stress-strain of specimens was measured by TENSOMETER 2000. A speed of measurement was 200[mm/min], ranges of stress and strain were 400(Kgf/cm^2) and 600[ %]. In addition, tests of stress-strain were progressed by aging specimens at air oven. Finally surface profile was shown in order to looking for protrusion of specimens by using smoothness tester. Density was highly measured according to increasing the content of carbon black from this experimental result, and stress was decreased, while strain was increased according to increasing the content of carbon black. And stress-strain were decreased some after aging because of oxidation reaction of chemical defect. Lastly surface of specimens smoothed generally. |