Electrical AC Insulation Breakdown Characteristics of Various Epoxy/ Heterogeneous Inorganic Mixed Composite |
| DOI |
http://doi.org/10.5370/KIEE.2018.67.11.1463 |
| Keywords |
Environment-friendly insulation gas ; Mixed heterogeneous inorganic composite ; Epoxy resin ; Interfacial property ; AC insulation breakdown strength |
| Abstract |
In this study, 20 types of samples were prepared by mixing different kinds of inorganic materials to develop insulation materials for epoxy - based GIS substation equipment used under high voltage environmentally friendly insulation gas. One of the electrical characteristics, AC insulation breakdown experiment was performed. As mixing ratio of mixed heterogeneous inorganic materials, the dielectric breakdown strength was increased with increasing filler ratio of micro silica , micro silica : micro Alumina, 1:9, 3:7, 5:5, 7:3, 9:1, and decreased as the filling amount of micro alumina increased. The AC insulation breakdown characteristics were the best when the composition ratio was 9:1. The higher the content of silica, the better the interfacial properties, and the larger the alumina content ratio, the worse the interfacial properties. |